TOPDA Polyvinylidene fluoride (PVDF) resin mainly refers to the homopolymer of vinylidene fluoride or the copolymer of vinylidene fluoride and a small amount of other vinylidene fluoride monomers. It has the characteristics of both fluororesin and general resin. The resin itself has good chemical corrosion resistance, high temperature resistance, oxidation resistance, weather resistance, radiation resistance, as well as piezoelectric, dielectric, thermoelectric and other special properties, so it is widely used in high-end functional films such as piezoelectric film, solar back plate film, lithium battery diaphragm, etc.
| Product Name | Code | Main Features | Main Technical Index | Applications |
| PVDF Powder For Coating | TPD-F201 | Purity: ＞99.5% Scattered fineness: 25µm Melting Index: 0.5-2.0g/10min Relative density: 1.75-1.77g/cm3 Melting point: 156-165℃ | 1. Excellent corrosion resistance 2. Good ultraviolet ray and radiation resistance 3. Excellent weather resistance 4. Excellent processing properties 5. Free of PFOA | Used to produce fluorocarbon coatings. |
|
| TPD-F202 | Viscosity: 3000-8500mPa.S Relative density: 1.75-1.77 Melting Point: 156-165℃ | 1. Soluble in polar organic solvents 2. Good chemical resistance 3. High viscosity and strong adhesion 4. Easy to form film 5. Good processability | Mainly used as electrode binder for lithium battery. |
| TPD-F202B | Viscosity: ＞8500mPa.S Relative density: 1.75-1.77 Melting Point: 156-165℃ | |||
| PVDF Resin For Powder Coating | TPD-F203 | Purity: ＞99.99% Melting index: 5.0-15.0g/10min Volume density: 300-500g/cm3 Melting Point: 165-175℃ | 1. Low melting viscosity 2. High mass flow rate 3. Excellent corrosion resistance 4. Excellent ultraviolet and radiation resistance | Mainly used in powder coating. |
| PVDF Resin For Membrane | TPD-F204 | Viscosity: ≥150mpa.s Melting Index: 2.0-7.0g/10min Relative density: 1.77-1.79g/cm3 Melting Point: 165-175℃ | 1. Excellent chemical and solvent resistance 2. Good mechanical strength and high toughness 3. Good solubility in some kinds of solvents | Used to produce PVDF membrane. |
| PVDF Resin For Extrusion & Moulding | TPD-F205 | Melting index: 1.0-25.0g/10min Tensile Strength: ≥35.0Mpa Elongation at break: ≥25% Hardness: 70-80 Shore D | 1. High melting viscosity 2. Good mechanical strength and high toughness 3. Excellent chemical resistance | Suitable for producing PVDF products by extrusion and moulding processes. |
|
| TPD-F206-1 | Melting index: 3.1-7.0g/10min Tensile Strength: 35.0Mpa Elongation at break: 25% |
1. Low melting viscosity 2. Good mechanical strength and high toughness
|
Suitable for producing PVDF products by injection and extrusion processes. |
| TPD-F206-2 | Melting index: 7.1-14.0g/10min Tensile Strength: 35.0Mpa Elongation at break: 25% | |||
| TPD-F206-3 | Melting index: 14.1-25.0g/10min Tensile Strength: 35.0Mpa Elongation at break: 25% | |||
| TPD-F206-4 | Melting index: ≥25.1g/10min Tensile Strength: 35.0Mpa Elongation at break: 25% |